#$Date: 2016-02-13 21:28:24 +0200 (Sat, 13 Feb 2016) $
#$Revision: 176429 $
#$URL: svn://www.crystallography.net/cod/cif/7/11/72/7117217.cif $
#------------------------------------------------------------------------------
#
# This file is available in the Crystallography Open Database (COD),
# http://www.crystallography.net/
#
# All data on this site have been placed in the public domain by the
# contributors.
#
data_7117217
loop_
_publ_author_name
'Vadim M. Kovrugin'
'Marie Colmont'
'Oleg I. Siidra'
'Olivier Mentre'
'Alexander Al-Shuray'
'Vladislav V. Gurzhiy'
'Sergey V. Krivovichev'
_publ_section_title
;
 Oxocentered Cu(II) lead selenite honeycomb lattices hosting Cu(I)Cl2
 groups obtained by chemical vapor transport reactions
;
_journal_name_full               Chem.Commun.
_journal_page_first              9563
_journal_paper_doi               10.1039/C5cc01426C
_journal_volume                  51
_journal_year                    2015
_chemical_formula_moiety
'Cl7.60 Cu11.60 O16 Pb0.40 Se4, 2(Cl2 Cu), 1.6(K)'
_chemical_formula_sum            'Cl11.6 Cu13.6 K1.6 O16 Pb0.4 Se4'
_chemical_formula_weight         1992.64
_chemical_name_systematic
;
 ?
;
_space_group_crystal_system      monoclinic
_space_group_IT_number           12
_space_group_name_Hall           '-C 2y'
_space_group_name_H-M_alt        'C 1 2/m 1'
_symmetry_space_group_name_Hall  '-C 2y'
_symmetry_space_group_name_H-M   'C 1 2/m 1'
_atom_sites_solution_hydrogens   .
_audit_creation_method           SHELXL-97
_cell_angle_alpha                90
_cell_angle_beta                 95.965(5)
_cell_angle_gamma                90
_cell_formula_units_Z            1
_cell_length_a                   15.1158(11)
_cell_length_b                   6.1853(4)
_cell_length_c                   9.2672(9)
_cell_measurement_reflns_used    1863
_cell_measurement_temperature    293(2)
_cell_measurement_theta_max      29.02
_cell_measurement_theta_min      2.21
_cell_volume                     861.75(12)
_computing_cell_refinement       'Bruker SAINT'
_computing_data_collection       'Bruker APEX2'
_computing_data_reduction        'Bruker SAINT'
_computing_molecular_graphics    'ATOMS (Dowty, 2000)'
_computing_structure_refinement  'SHELXL-2013 (Sheldrick, 2013)'
_computing_structure_solution    'Superflip (Palatinus & Chapuis, 2007)'
_diffrn_ambient_temperature      293(2)
_diffrn_measured_fraction_theta_full 0.995
_diffrn_measured_fraction_theta_max 0.995
_diffrn_measurement_device_type  'Bruker APEX-II CCD'
_diffrn_measurement_method       'φ and ω scans'
_diffrn_radiation_source         'fine-focus sealed tube'
_diffrn_radiation_type           MoK\a
_diffrn_radiation_wavelength     0.71073
_diffrn_reflns_av_R_equivalents  0.0301
_diffrn_reflns_av_unetI/netI     0.0393
_diffrn_reflns_Laue_measured_fraction_full 0.995
_diffrn_reflns_Laue_measured_fraction_max 0.995
_diffrn_reflns_limit_h_max       21
_diffrn_reflns_limit_h_min       -21
_diffrn_reflns_limit_k_max       8
_diffrn_reflns_limit_k_min       -7
_diffrn_reflns_limit_l_max       13
_diffrn_reflns_limit_l_min       -10
_diffrn_reflns_number            5430
_diffrn_reflns_point_group_measured_fraction_full 0.995
_diffrn_reflns_point_group_measured_fraction_max 0.995
_diffrn_reflns_theta_full        25.242
_diffrn_reflns_theta_max         31.044
_diffrn_reflns_theta_min         2.210
_exptl_absorpt_coefficient_mu    15.516
_exptl_absorpt_correction_T_max  0.7462
_exptl_absorpt_correction_T_min  0.6129
_exptl_absorpt_correction_type   multi-scan
_exptl_absorpt_process_details   'Bruker SADABS'
_exptl_crystal_colour            brown
_exptl_crystal_density_diffrn    3.840
_exptl_crystal_description       needle
_exptl_crystal_F_000             919
_exptl_crystal_size_max          0.26
_exptl_crystal_size_mid          0.18
_exptl_crystal_size_min          0.14
_refine_diff_density_max         4.247
_refine_diff_density_min         -1.986
_refine_diff_density_rms         0.278
_refine_ls_extinction_coef       0.0012(4)
_refine_ls_extinction_expression Fc^*^=kFc[1+0.001xFc²λ³/sin(2θ)]^-1/4^
_refine_ls_extinction_method     SHELXL
_refine_ls_goodness_of_fit_ref   1.070
_refine_ls_hydrogen_treatment    undef
_refine_ls_matrix_type           full
_refine_ls_number_parameters     79
_refine_ls_number_reflns         1479
_refine_ls_number_restraints     0
_refine_ls_restrained_S_all      1.070
_refine_ls_R_factor_all          0.0606
_refine_ls_R_factor_gt           0.0453
_refine_ls_shift/su_max          0.000
_refine_ls_shift/su_mean         0.000
_refine_ls_structure_factor_coef Fsqd
_refine_ls_weighting_details
'w=1/[σ²(Fo²)+(0.0648P)²+8.8960P] where P=(Fo²+2Fc²)/3'
_refine_ls_weighting_scheme      calc
_refine_ls_wR_factor_gt          0.1162
_refine_ls_wR_factor_ref         0.1246
_reflns_Friedel_coverage         0.000
_reflns_Friedel_fraction_full    .
_reflns_Friedel_fraction_max     .
_reflns_number_gt                1190
_reflns_number_total             1479
_reflns_threshold_expression     'I > 2σ(I)'
_cod_data_source_file            c5cc01426c2-4.cif
_cod_data_source_block           shelx_3
_cod_original_formula_sum        'Cl11.60 Cu13.60 K1.60 O16 Pb0.40 Se4'
_cod_database_code               7117217
#BEGIN Tags that were not found in dictionaries:
_shelx_space_group_comment
;
The symmetry employed for this shelxl refinement is uniquely defined
by the following loop, which should always be used as a source of
symmetry information in preference to the above space-group names.
They are only intended as comments.
;
#END Tags that were not found in dictionaries
loop_
_space_group_symop_operation_xyz
'x, y, z'
'-x, y, -z'
'x+1/2, y+1/2, z'
'-x+1/2, y+1/2, -z'
'-x, -y, -z'
'x, -y, z'
'-x+1/2, -y+1/2, -z'
'x+1/2, -y+1/2, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_adp_type
_atom_site_occupancy
_atom_site_site_symmetry_order
_atom_site_calc_flag
_atom_site_refinement_flags_posn
_atom_site_refinement_flags_adp
_atom_site_refinement_flags_occupancy
_atom_site_disorder_assembly
_atom_site_disorder_group
Se1 Se 0.35740(5) 0.0000 0.25910(8) 0.0149(2) Uani 1 2 d S T P . .
Cu1 Cu 0.42896(6) 0.0000 0.61039(11) 0.0201(3) Uani 1 2 d S T P . .
Cu2 Cu 0.2500 0.2500 0.5000 0.0170(2) Uani 1 2 d S . P . .
Cu3 Cu 0.0000 0.0000 0.5000 0.0518(6) Uani 1 4 d S T P . .
Cu4 Cu 0.26172(9) 0.0000 0.77936(17) 0.0212(3) Uani 0.9 2 d S T P . .
Pb1 Pb 0.2666(2) 0.0000 0.8453(4) 0.0172(7) Uani 0.1 2 d S T P . .
K1 K 0.5000 0.5000 1.0000 0.0477(11) Uani 0.8 4 d S T P . .
Cl1 Cl 0.09713(17) 0.0000 0.3571(3) 0.0411(6) Uani 1 2 d S T P . .
Cl2 Cl 0.42217(16) 0.0000 0.8552(2) 0.0322(5) Uani 1 2 d S T P . .
Cl3 Cl 0.30213(17) -0.5000 0.0198(3) 0.0369(6) Uani 0.9 2 d S T P . .
O1 O 0.4433(3) 0.0000 0.3972(7) 0.0231(12) Uani 1 2 d S T P . .
O2 O 0.3008(3) 0.2147(7) 0.3143(5) 0.0231(9) Uani 1 1 d . . . . .
O3 O 0.3034(3) 0.0000 0.5919(6) 0.0147(10) Uani 1 2 d S T P . .
loop_
_atom_type_symbol
_atom_type_description
_atom_type_scat_dispersion_real
_atom_type_scat_dispersion_imag
_atom_type_scat_source
O O 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Cl Cl 0.1484 0.1585 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
K K 0.2009 0.2494 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Cu Cu 0.3201 1.2651 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Se Se -0.0929 2.2259 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Pb Pb -3.3944 10.1111 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
O2 Se1 O2 103.7(3) . 6
O2 Se1 O1 98.11(19) . .
O2 Se1 O1 98.11(19) 6 .
O2 Se1 O3 61.96(15) . .
O2 Se1 O3 61.96(15) 6 .
O1 Se1 O3 62.8(2) . .
O3 Cu1 O1 172.8(3) . 5_656
O3 Cu1 O1 96.9(2) . .
O1 Cu1 O1 75.8(3) 5_656 .
O3 Cu1 Cl2 86.65(18) . .
O1 Cu1 Cl2 100.6(2) 5_656 .
O1 Cu1 Cl2 176.41(16) . .
O3 Cu1 O2 56.80(17) . 6
O1 Cu1 O2 116.70(19) 5_656 6
O1 Cu1 O2 47.80(15) . 6
Cl2 Cu1 O2 135.24(9) . 6
O3 Cu1 O2 56.80(17) . .
O1 Cu1 O2 116.70(19) 5_656 .
O1 Cu1 O2 47.80(15) . .
Cl2 Cu1 O2 135.24(9) . .
O2 Cu1 O2 45.19(15) 6 .
O3 Cu2 O3 180.0 7_556 .
O3 Cu2 O2 96.6(2) 7_556 7_556
O3 Cu2 O2 83.4(2) . 7_556
O3 Cu2 O2 83.4(2) 7_556 .
O3 Cu2 O2 96.6(2) . .
O2 Cu2 O2 180.0 7_556 .
O3 Cu2 Cu4 141.96(16) 7_556 .
O3 Cu2 Cu4 38.04(16) . .
O2 Cu2 Cu4 45.35(12) 7_556 .
O2 Cu2 Cu4 134.65(12) . .
O3 Cu2 Cu4 38.04(16) 7_556 7_556
O3 Cu2 Cu4 141.96(16) . 7_556
O2 Cu2 Cu4 134.65(12) 7_556 7_556
O2 Cu2 Cu4 45.35(12) . 7_556
Cu4 Cu2 Cu4 180.0 . 7_556
O3 Cu2 O2 123.72(16) 7_556 6
O3 Cu2 O2 56.28(16) . 6
O2 Cu2 O2 130.61(17) 7_556 6
O2 Cu2 O2 49.39(17) . 6
Cu4 Cu2 O2 90.27(7) . 6
Cu4 Cu2 O2 89.73(7) 7_556 6
O3 Cu2 O2 56.28(16) 7_556 4_556
O3 Cu2 O2 123.72(16) . 4_556
O2 Cu2 O2 49.39(17) 7_556 4_556
O2 Cu2 O2 130.61(17) . 4_556
Cu4 Cu2 O2 89.73(7) . 4_556
Cu4 Cu2 O2 90.27(7) 7_556 4_556
O2 Cu2 O2 180.0 6 4_556
O3 Cu2 O1 55.91(17) 7_556 7_556
O3 Cu2 O1 124.09(17) . 7_556
O2 Cu2 O1 45.98(15) 7_556 7_556
O2 Cu2 O1 134.02(15) . 7_556
Cu4 Cu2 O1 88.24(9) . 7_556
Cu4 Cu2 O1 91.76(9) 7_556 7_556
O2 Cu2 O1 136.77(9) 6 7_556
O2 Cu2 O1 43.23(9) 4_556 7_556
O3 Cu2 O1 124.09(17) 7_556 .
O3 Cu2 O1 55.91(17) . .
O2 Cu2 O1 134.02(15) 7_556 .
O2 Cu2 O1 45.98(15) . .
Cu4 Cu2 O1 91.76(9) . .
Cu4 Cu2 O1 88.24(9) 7_556 .
O2 Cu2 O1 43.23(9) 6 .
O2 Cu2 O1 136.77(9) 4_556 .
O1 Cu2 O1 180.0 7_556 .
Cl1 Cu3 Cl1 180.0 5_556 .
Cl1 Cu3 O1 89.76(10) 5_556 7_556
Cl1 Cu3 O1 90.24(10) . 7_556
Cl1 Cu3 O1 90.24(10) 5_556 3_445
Cl1 Cu3 O1 89.76(10) . 3_445
O1 Cu3 O1 180.0 7_556 3_445
Cl1 Cu3 O1 90.24(10) 5_556 3_455
Cl1 Cu3 O1 89.76(10) . 3_455
O1 Cu3 O1 42.85(18) 7_556 3_455
O1 Cu3 O1 137.15(18) 3_445 3_455
Cl1 Cu3 O1 89.76(10) 5_556 7_546
Cl1 Cu3 O1 90.24(10) . 7_546
O1 Cu3 O1 137.15(18) 7_556 7_546
O1 Cu3 O1 42.85(18) 3_445 7_546
O1 Cu3 O1 180.0 3_455 7_546
Cl1 Cu3 O2 107.14(10) 5_556 7_556
Cl1 Cu3 O2 72.86(10) . 7_556
O1 Cu3 O2 42.22(11) 7_556 7_556
O1 Cu3 O2 137.78(11) 3_445 7_556
O1 Cu3 O2 82.21(11) 3_455 7_556
O1 Cu3 O2 97.79(11) 7_546 7_556
Cl1 Cu3 O2 72.86(10) 5_556 3_445
Cl1 Cu3 O2 107.14(10) . 3_445
O1 Cu3 O2 137.78(11) 7_556 3_445
O1 Cu3 O2 42.22(11) 3_445 3_445
O1 Cu3 O2 97.79(11) 3_455 3_445
O1 Cu3 O2 82.21(11) 7_546 3_445
O2 Cu3 O2 180.00(9) 7_556 3_445
Cl1 Cu3 O2 72.86(10) 5_556 8_455
Cl1 Cu3 O2 107.14(10) . 8_455
O1 Cu3 O2 82.21(11) 7_556 8_455
O1 Cu3 O2 97.79(11) 3_445 8_455
O1 Cu3 O2 42.22(11) 3_455 8_455
O1 Cu3 O2 137.78(11) 7_546 8_455
O2 Cu3 O2 123.86(12) 7_556 8_455
O2 Cu3 O2 56.14(12) 3_445 8_455
Cl1 Cu3 O2 107.14(10) 5_556 4_546
Cl1 Cu3 O2 72.86(10) . 4_546
O1 Cu3 O2 97.79(11) 7_556 4_546
O1 Cu3 O2 82.21(11) 3_445 4_546
O1 Cu3 O2 137.78(11) 3_455 4_546
O1 Cu3 O2 42.22(11) 7_546 4_546
O2 Cu3 O2 56.14(12) 7_556 4_546
O2 Cu3 O2 123.86(12) 3_445 4_546
O2 Cu3 O2 180.00(12) 8_455 4_546
Pb1 Cu4 O3 153.9(5) . .
Pb1 Cu4 O2 114.2(2) . 4_546
O3 Cu4 O2 78.73(15) . 4_546
Pb1 Cu4 O2 114.2(2) . 7_556
O3 Cu4 O2 78.73(14) . 7_556
O2 Cu4 O2 110.9(3) 4_546 7_556
Pb1 Cu4 Cl3 33.0(4) . 7_546
O3 Cu4 Cl3 173.10(19) . 7_546
O2 Cu4 Cl3 97.48(12) 4_546 7_546
O2 Cu4 Cl3 97.48(12) 7_556 7_546
Pb1 Cu4 Cl2 72.5(4) . .
O3 Cu4 Cl2 81.39(17) . .
O2 Cu4 Cl2 119.80(13) 4_546 .
O2 Cu4 Cl2 119.80(13) 7_556 .
Cl3 Cu4 Cl2 105.50(11) 7_546 .
Pb1 Cu4 Cu2 148.90(4) . 4_546
O3 Cu4 Cu2 37.94(9) . 4_546
O2 Cu4 Cu2 40.79(11) 4_546 4_546
O2 Cu4 Cu2 95.20(13) 7_556 4_546
Cl3 Cu4 Cu2 137.95(6) 7_546 4_546
Cl2 Cu4 Cu2 102.39(6) . 4_546
Pb1 Cu4 Cu2 148.90(4) . .
O3 Cu4 Cu2 37.94(9) . .
O2 Cu4 Cu2 95.20(13) 4_546 .
O2 Cu4 Cu2 40.79(11) 7_556 .
Cl3 Cu4 Cu2 137.95(6) 7_546 .
Cl2 Cu4 Cu2 102.39(6) . .
Cu2 Cu4 Cu2 61.94(3) 4_546 .
Cu4 Pb1 Cl3 135.8(5) . 7_546
Cu4 Pb1 Cl2 93.2(4) . .
Cl3 Pb1 Cl2 131.0(2) 7_546 .
Cu4 Pb1 O2 52.8(2) . 4_546
Cl3 Pb1 O2 101.28(17) 7_546 4_546
Cl2 Pb1 O2 112.02(16) . 4_546
Cu4 Pb1 O2 52.8(2) . 7_556
Cl3 Pb1 O2 101.28(17) 7_546 7_556
Cl2 Pb1 O2 112.02(16) . 7_556
O2 Pb1 O2 91.9(3) 4_546 7_556
Cu4 Pb1 O3 19.9(4) . .
Cl3 Pb1 O3 155.7(3) 7_546 .
Cl2 Pb1 O3 73.29(17) . .
O2 Pb1 O3 63.08(15) 4_546 .
O2 Pb1 O3 63.08(15) 7_556 .
Cl3 K1 Cl3 180.0 5_656 1_566
Cl3 K1 Cl1 74.62(7) 5_656 3_556
Cl3 K1 Cl1 105.38(7) 1_566 3_556
Cl3 K1 Cl1 105.38(7) 5_656 7_556
Cl3 K1 Cl1 74.62(7) 1_566 7_556
Cl1 K1 Cl1 180.0 3_556 7_556
Cl3 K1 Cl2 105.71(4) 5_656 .
Cl3 K1 Cl2 74.29(4) 1_566 .
Cl1 K1 Cl2 116.97(3) 3_556 .
Cl1 K1 Cl2 63.03(3) 7_556 .
Cl3 K1 Cl2 74.29(4) 5_656 5_667
Cl3 K1 Cl2 105.71(4) 1_566 5_667
Cl1 K1 Cl2 63.03(3) 3_556 5_667
Cl1 K1 Cl2 116.97(3) 7_556 5_667
Cl2 K1 Cl2 180.0 . 5_667
Cl3 K1 Cl2 74.29(4) 5_656 5_657
Cl3 K1 Cl2 105.71(4) 1_566 5_657
Cl1 K1 Cl2 63.03(3) 3_556 5_657
Cl1 K1 Cl2 116.97(3) 7_556 5_657
Cl2 K1 Cl2 57.32(7) . 5_657
Cl2 K1 Cl2 122.68(7) 5_667 5_657
Cl3 K1 Cl2 105.71(4) 5_656 1_565
Cl3 K1 Cl2 74.29(4) 1_566 1_565
Cl1 K1 Cl2 116.97(3) 3_556 1_565
Cl1 K1 Cl2 63.03(3) 7_556 1_565
Cl2 K1 Cl2 122.68(7) . 1_565
Cl2 K1 Cl2 57.32(7) 5_667 1_565
Cl2 K1 Cl2 180.0 5_657 1_565
Cl3 K1 O2 137.27(7) 5_656 6_566
Cl3 K1 O2 42.73(6) 1_566 6_566
Cl1 K1 O2 69.37(7) 3_556 6_566
Cl1 K1 O2 110.63(7) 7_556 6_566
Cl2 K1 O2 110.63(6) . 6_566
Cl2 K1 O2 69.37(6) 5_667 6_566
Cl2 K1 O2 107.50(7) 5_657 6_566
Cl2 K1 O2 72.50(7) 1_565 6_566
Cl3 K1 O2 137.27(6) 5_656 1_556
Cl3 K1 O2 42.73(6) 1_566 1_556
Cl1 K1 O2 69.37(7) 3_556 1_556
Cl1 K1 O2 110.63(7) 7_556 1_556
Cl2 K1 O2 72.50(7) . 1_556
Cl2 K1 O2 107.50(7) 5_667 1_556
Cl2 K1 O2 69.37(6) 5_657 1_556
Cl2 K1 O2 110.63(6) 1_565 1_556
O2 K1 O2 43.69(10) 6_566 1_556
Cl3 K1 O2 42.73(6) 5_656 5_666
Cl3 K1 O2 137.27(6) 1_566 5_666
Cl1 K1 O2 110.63(7) 3_556 5_666
Cl1 K1 O2 69.37(7) 7_556 5_666
Cl2 K1 O2 107.50(7) . 5_666
Cl2 K1 O2 72.50(7) 5_667 5_666
Cl2 K1 O2 110.63(6) 5_657 5_666
Cl2 K1 O2 69.37(6) 1_565 5_666
O2 K1 O2 136.31(10) 6_566 5_666
O2 K1 O2 180.0 1_556 5_666
Cl3 K1 O2 42.73(6) 5_656 2_656
Cl3 K1 O2 137.27(7) 1_566 2_656
Cl1 K1 O2 110.63(7) 3_556 2_656
Cl1 K1 O2 69.37(7) 7_556 2_656
Cl2 K1 O2 69.37(6) . 2_656
Cl2 K1 O2 110.63(6) 5_667 2_656
Cl2 K1 O2 72.50(7) 5_657 2_656
Cl2 K1 O2 107.50(7) 1_565 2_656
O2 K1 O2 180.0 6_566 2_656
O2 K1 O2 136.31(10) 1_556 2_656
O2 K1 O2 43.69(10) 5_666 2_656
Cu3 Cl1 O2 141.26(13) . 6
Cu3 Cl1 O2 141.26(13) . .
O2 Cl1 O2 45.79(14) 6 .
Cu3 Cl1 O3 103.86(10) . 7_556
O2 Cl1 O3 88.81(11) 6 7_556
O2 Cl1 O3 44.09(11) . 7_556
Cu3 Cl1 O3 103.86(10) . 7_546
O2 Cl1 O3 44.09(11) 6 7_546
O2 Cl1 O3 88.81(11) . 7_546
O3 Cl1 O3 127.41(17) 7_556 7_546
Cu3 Cl1 K1 110.50(10) . 3_444
O2 Cl1 K1 100.72(10) 6 3_444
O2 Cl1 K1 100.72(10) . 3_444
O3 Cl1 K1 105.37(10) 7_556 3_444
O3 Cl1 K1 105.37(10) 7_546 3_444
Cu1 Cl2 Pb1 96.31(14) . .
Cu1 Cl2 Cu4 81.99(8) . .
Pb1 Cl2 Cu4 14.32(9) . .
Cu1 Cl2 O3 40.96(11) . .
Pb1 Cl2 O3 55.35(15) . .
Cu4 Cl2 O3 41.03(11) . .
Cu1 Cl2 O1 35.86(11) . 5_656
Pb1 Cl2 O1 132.17(17) . 5_656
Cu4 Cl2 O1 117.85(13) . 5_656
O3 Cl2 O1 76.82(15) . 5_656
Cu1 Cl2 K1 109.33(5) . .
Pb1 Cl2 K1 107.98(6) . .
Cu4 Cl2 K1 112.95(4) . .
O3 Cl2 K1 118.52(3) . .
O1 Cl2 K1 93.72(6) 5_656 .
Cu1 Cl2 K1 109.33(5) . 1_545
Pb1 Cl2 K1 107.98(6) . 1_545
Cu4 Cl2 K1 112.95(4) . 1_545
O3 Cl2 K1 118.52(3) . 1_545
O1 Cl2 K1 93.72(6) 5_656 1_545
K1 Cl2 K1 122.68(7) . 1_545
Pb1 Cl3 Cu4 11.18(14) 7_546 7_546
Pb1 Cl3 K1 136.70(19) 7_546 1_544
Cu4 Cl3 K1 125.52(12) 7_546 1_544
Pb1 Cl3 O2 47.76(13) 7_546 6
Cu4 Cl3 O2 40.78(8) 7_546 6
K1 Cl3 O2 98.28(10) 1_544 6
Pb1 Cl3 O2 47.76(13) 7_546 1_545
Cu4 Cl3 O2 40.78(8) 7_546 1_545
K1 Cl3 O2 98.28(10) 1_544 1_545
O2 Cl3 O2 65.73(16) 6 1_545
Se1 O1 Cu1 130.4(4) . 5_656
Se1 O1 Cu1 125.4(3) . .
Cu1 O1 Cu1 104.2(3) 5_656 .
Se1 O1 O1 176.2(5) . 5_656
Cu1 O1 O1 53.4(2) 5_656 5_656
Cu1 O1 O1 50.8(2) . 5_656
Se1 O1 O2 40.39(13) . .
Cu1 O1 O2 142.5(2) 5_656 .
Cu1 O1 O2 96.9(2) . .
O1 O1 O2 137.2(3) 5_656 .
Se1 O1 O2 40.39(13) . 6
Cu1 O1 O2 142.5(2) 5_656 6
Cu1 O1 O2 96.9(2) . 6
O1 O1 O2 137.2(3) 5_656 6
O2 O1 O2 62.0(2) . 6
Se1 O1 O3 85.5(2) . .
Cu1 O1 O3 144.1(3) 5_656 .
Cu1 O1 O3 39.94(15) . .
O1 O1 O3 90.7(3) 5_656 .
O2 O1 O3 63.11(17) . .
O2 O1 O3 63.11(17) 6 .
Se1 O1 Cl2 86.9(2) . 5_656
Cu1 O1 Cl2 43.54(14) 5_656 5_656
Cu1 O1 Cl2 147.7(2) . 5_656
O1 O1 Cl2 96.9(3) 5_656 5_656
O2 O1 Cl2 110.6(2) . 5_656
O2 O1 Cl2 110.6(2) 6 5_656
O3 O1 Cl2 172.3(2) . 5_656
Se1 O1 Cu3 111.38(9) . 3
Cu1 O1 Cu3 77.42(10) 5_656 3
Cu1 O1 Cu3 76.65(11) . 3
O1 O1 Cu3 68.57(9) 5_656 3
O2 O1 Cu3 77.81(11) . 3
O2 O1 Cu3 138.37(18) 6 3
O3 O1 Cu3 90.27(12) . 3
Cl2 O1 Cu3 92.53(10) 5_656 3
Se1 O1 Cu3 111.38(9) . 3_545
Cu1 O1 Cu3 77.42(10) 5_656 3_545
Cu1 O1 Cu3 76.65(11) . 3_545
O1 O1 Cu3 68.57(9) 5_656 3_545
O2 O1 Cu3 138.37(18) . 3_545
O2 O1 Cu3 77.81(11) 6 3_545
O3 O1 Cu3 90.27(12) . 3_545
Cl2 O1 Cu3 92.53(10) 5_656 3_545
Cu3 O1 Cu3 137.15(18) 3 3_545
Se1 O1 Cu2 67.64(15) . 4_546
Cu1 O1 Cu2 150.06(14) 5_656 4_546
Cu1 O1 Cu2 63.72(13) . 4_546
O1 O1 Cu2 109.0(3) 5_656 4_546
O2 O1 Cu2 67.42(15) . 4_546
O2 O1 Cu2 33.28(11) 6 4_546
O3 O1 Cu2 32.71(8) . 4_546
Cl2 O1 Cu2 142.36(14) 5_656 4_546
Cu3 O1 Cu2 121.85(15) 3 4_546
Cu3 O1 Cu2 73.17(6) 3_545 4_546
Se1 O1 Cu2 67.64(15) . .
Cu1 O1 Cu2 150.06(14) 5_656 .
Cu1 O1 Cu2 63.72(13) . .
O1 O1 Cu2 109.0(3) 5_656 .
O2 O1 Cu2 33.28(11) . .
O2 O1 Cu2 67.42(15) 6 .
O3 O1 Cu2 32.71(8) . .
Cl2 O1 Cu2 142.36(14) 5_656 .
Cu3 O1 Cu2 73.17(6) 3 .
Cu3 O1 Cu2 121.85(15) 3_545 .
Cu2 O1 Cu2 52.07(8) 4_546 .
Se1 O2 Cu2 127.5(2) . .
Se1 O2 Cu4 137.8(2) . 7_556
Cu2 O2 Cu4 93.86(17) . 7_556
Se1 O2 Pb1 125.1(2) . 7_556
Cu2 O2 Pb1 105.79(19) . 7_556
Cu4 O2 Pb1 13.05(7) 7_556 7_556
Se1 O2 O1 41.49(15) . .
Cu2 O2 O1 100.7(2) . .
Cu4 O2 O1 149.8(2) 7_556 .
Pb1 O2 O1 146.2(2) 7_556 .
Se1 O2 O3 171.3(3) . 7_556
Cu2 O2 O3 47.25(14) . 7_556
Cu4 O2 O3 46.61(14) 7_556 7_556
Pb1 O2 O3 58.72(17) 7_556 7_556
O1 O2 O3 140.7(2) . 7_556
Se1 O2 O2 38.13(15) . 6
Cu2 O2 O2 96.38(13) . 6
Cu4 O2 O2 145.46(13) 7_556 6
Pb1 O2 O2 135.96(13) 7_556 6
O1 O2 O2 59.01(12) . 6
O3 O2 O2 133.25(13) 7_556 6
Se1 O2 O3 87.02(17) . .
Cu2 O2 O3 40.86(11) . .
Cu4 O2 O3 134.72(19) 7_556 .
Pb1 O2 O3 146.4(2) 7_556 .
O1 O2 O3 64.19(18) . .
O3 O2 O3 88.11(15) 7_556 .
O2 O2 O3 62.66(10) 6 .
Se1 O2 Cl3 97.16(17) . 1_565
Cu2 O2 Cl3 135.29(18) . 1_565
Cu4 O2 Cl3 41.74(9) 7_556 1_565
Pb1 O2 Cl3 30.96(11) 7_556 1_565
O1 O2 Cl3 116.84(19) . 1_565
O3 O2 Cl3 88.20(16) 7_556 1_565
O2 O2 Cl3 122.87(8) 6 1_565
O3 O2 Cl3 174.35(18) . 1_565
Se1 O2 Cl1 102.78(19) . .
Cu2 O2 Cl1 60.21(12) . .
Cu4 O2 Cl1 90.15(14) 7_556 .
Pb1 O2 Cl1 91.55(15) 7_556 .
O1 O2 Cl1 120.05(17) . .
O3 O2 Cl1 68.71(13) 7_556 .
O2 O2 Cl1 67.11(7) 6 .
O3 O2 Cl1 69.35(14) . .
Cl3 O2 Cl1 113.14(14) 1_565 .
Se1 O2 Cu1 71.24(14) . .
Cu2 O2 Cu1 65.54(11) . .
Cu4 O2 Cu1 145.64(19) 7_556 .
Pb1 O2 Cu1 156.62(19) 7_556 .
O1 O2 Cu1 35.26(15) . .
O3 O2 Cu1 107.91(18) 7_556 .
O2 O2 Cu1 67.40(7) 6 .
O3 O2 Cu1 33.11(11) . .
Cl3 O2 Cu1 145.38(15) 1_565 .
Cl1 O2 Cu1 101.33(12) . .
Se1 O2 Cu2 69.19(14) . 4_546
Cu2 O2 Cu2 62.15(11) . 4_546
Cu4 O2 Cu2 140.44(18) 7_556 4_546
Pb1 O2 Cu2 142.52(18) 7_556 4_546
O1 O2 Cu2 69.36(13) . 4_546
O3 O2 Cu2 103.03(16) 7_556 4_546
O2 O2 Cu2 34.23(7) 6 4_546
O3 O2 Cu2 33.21(8) . 4_546
Cl3 O2 Cu2 152.26(15) 1_565 4_546
Cl1 O2 Cu2 51.15(7) . 4_546
Cu1 O2 Cu2 54.81(6) . 4_546
Cu1 O3 Cu2 114.60(17) . 4_546
Cu1 O3 Cu2 114.60(17) . .
Cu2 O3 Cu2 108.6(3) 4_546 .
Cu1 O3 Cu4 110.0(3) . .
Cu2 O3 Cu4 104.02(19) 4_546 .
Cu2 O3 Cu4 104.02(19) . .
Cu1 O3 Pb1 103.8(2) . .
Cu2 O3 Pb1 107.36(18) 4_546 .
Cu2 O3 Pb1 107.36(18) . .
Cu4 O3 Pb1 6.22(11) . .
Cu1 O3 O2 127.85(19) . 4_546
Cu2 O3 O2 49.36(12) 4_546 4_546
Cu2 O3 O2 117.5(3) . 4_546
Cu4 O3 O2 54.67(14) . 4_546
Pb1 O3 O2 58.20(15) . 4_546
Cu1 O3 O2 127.85(19) . 7_556
Cu2 O3 O2 117.5(3) 4_546 7_556
Cu2 O3 O2 49.36(12) . 7_556
Cu4 O3 O2 54.67(14) . 7_556
Pb1 O3 O2 58.20(15) . 7_556
O2 O3 O2 86.5(3) 4_546 7_556
Cu1 O3 Cl2 52.40(14) . .
Cu2 O3 Cl2 125.31(14) 4_546 .
Cu2 O3 Cl2 125.31(14) . .
Cu4 O3 Cl2 57.57(16) . .
Pb1 O3 Cl2 51.36(14) . .
O2 O3 Cl2 93.65(18) 4_546 .
O2 O3 Cl2 93.65(18) 7_556 .
Cu1 O3 O2 90.1(2) . 6
Cu2 O3 O2 42.53(13) 4_546 6
Cu2 O3 O2 90.5(2) . 6
Cu4 O3 O2 146.55(16) . 6
Pb1 O3 O2 149.60(13) . 6
O2 O3 O2 91.89(15) 4_546 6
O2 O3 O2 131.5(2) 7_556 6
Cl2 O3 O2 134.81(17) . 6
Cu1 O3 O2 90.1(2) . .
Cu2 O3 O2 90.5(2) 4_546 .
Cu2 O3 O2 42.53(13) . .
Cu4 O3 O2 146.55(16) . .
Pb1 O3 O2 149.60(13) . .
O2 O3 O2 131.5(2) 4_546 .
O2 O3 O2 91.89(15) 7_556 .
Cl2 O3 O2 134.81(17) . .
O2 O3 O2 54.7(2) 6 .
Cu1 O3 O1 43.12(16) . .
Cu2 O3 O1 91.39(18) 4_546 .
Cu2 O3 O1 91.39(18) . .
Cu4 O3 O1 153.1(3) . .
Pb1 O3 O1 146.9(3) . .
O2 O3 O1 135.73(14) 4_546 .
O2 O3 O1 135.73(14) 7_556 .
Cl2 O3 O1 95.52(19) . .
O2 O3 O1 52.69(15) 6 .
O2 O3 O1 52.69(15) . .
Cu1 O3 Se1 74.85(17) . .
Cu2 O3 Se1 73.38(16) 4_546 .
Cu2 O3 Se1 73.38(16) . .
Cu4 O3 Se1 175.2(2) . .
Pb1 O3 Se1 178.6(2) . .
O2 O3 Se1 122.62(17) 4_546 .
O2 O3 Se1 122.62(17) 7_556 .
Cl2 O3 Se1 127.24(18) . .
O2 O3 Se1 31.01(10) 6 .
O2 O3 Se1 31.01(10) . .
O1 O3 Se1 31.73(12) . .
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_distance
_geom_bond_site_symmetry_2
Se1 O2 1.688(4) .
Se1 O2 1.688(4) 6
Se1 O1 1.726(6) .
Se1 O3 3.271(6) .
Cu1 O3 1.887(5) .
Cu1 O1 1.940(5) 5_656
Cu1 O1 2.010(6) .
Cu1 Cl2 2.281(3) .
Cu1 O2 3.455(4) 6
Cu1 O2 3.455(4) .
Cu2 O3 1.904(3) 7_556
Cu2 O3 1.904(3) .
Cu2 O2 1.968(4) 7_556
Cu2 O2 1.968(4) .
Cu2 Cu4 3.0049(14) .
Cu2 Cu4 3.0049(14) 7_556
Cu2 O2 3.476(4) 6
Cu2 O2 3.476(4) 4_556
Cu2 O1 3.523(5) 7_556
Cu2 O1 3.523(5) .
Cu3 Cl1 2.077(3) 5_556
Cu3 Cl1 2.077(3) .
Cu3 O1 3.322(2) 7_556
Cu3 O1 3.322(2) 3_445
Cu3 O1 3.322(2) 3_455
Cu3 O1 3.322(2) 7_546
Cu3 O2 3.751(5) 7_556
Cu3 O2 3.751(5) 3_445
Cu3 O2 3.751(5) 8_455
Cu3 O2 3.751(5) 4_546
Cu4 Pb1 0.608(3) .
Cu4 O3 1.909(6) .
Cu4 O2 2.143(4) 4_546
Cu4 O2 2.143(4) 7_556
Cu4 Cl3 2.184(3) 7_546
Cu4 Cl2 2.454(3) .
Cu4 Cu2 3.0049(14) 4_546
Pb1 Cl3 1.706(5) 7_546
Pb1 Cl2 2.344(4) .
Pb1 O2 2.455(5) 4_546
Pb1 O2 2.455(5) 7_556
Pb1 O3 2.469(7) .
K1 Cl3 3.016(3) 5_656
K1 Cl3 3.016(3) 1_566
K1 Cl1 3.478(3) 3_556
K1 Cl1 3.478(3) 7_556
K1 Cl2 3.5245(11) .
K1 Cl2 3.5245(11) 5_667
K1 Cl2 3.5245(11) 5_657
K1 Cl2 3.5245(11) 1_565
K1 O2 4.743(4) 6_566
K1 O2 4.743(4) 1_556
K1 O2 4.743(4) 5_666
K1 O2 4.743(4) 2_656
Cl1 O2 3.413(5) 6
Cl1 O2 3.413(5) .
Cl1 O3 3.450(2) 7_556
Cl1 O3 3.450(2) 7_546
Cl1 K1 3.478(3) 3_444
Cl2 O3 2.874(6) .
Cl2 O1 3.255(6) 5_656
Cl2 K1 3.5245(11) 1_545
Cl3 Pb1 1.706(5) 7_546
Cl3 Cu4 2.184(3) 7_546
Cl3 K1 3.016(3) 1_544
Cl3 O2 3.252(5) 6
Cl3 O2 3.252(5) 1_545
O1 Cu1 1.940(5) 5_656
O1 O1 2.427(11) 5_656
O1 O2 2.579(6) .
O1 O2 2.579(6) 6
O1 O3 2.918(8) .
O1 Cl2 3.255(6) 5_656
O1 Cu3 3.322(2) 3
O1 Cu3 3.322(2) 3_545
O1 Cu2 3.523(5) 4_546
O2 Cu4 2.143(4) 7_556
O2 Pb1 2.455(5) 7_556
O2 O3 2.576(6) 7_556
O2 O2 2.655(9) 6
O2 O3 2.891(6) .
O2 Cl3 3.252(5) 1_565
O2 Cu2 3.476(4) 4_546
O3 Cu2 1.904(3) 4_546
O3 O2 2.576(6) 4_546
O3 O2 2.576(6) 7_556
O3 O2 2.891(6) 6