Information card for entry 4001270
Preview
| Coordinates | 4001270.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C4 H14 F5 In N2 |
|---|---|
| Calculated formula | C4 H14 F5 In N2 |
| Title of publication | Solvothermal Synthesis and Luminescent Properties of Two Organically Templated Chain-Structure Fluorides, [C4H14N2][MF5] (M = In, Sc) |
| Authors of publication | Jayasundera, Anil C. A.; Finch, Adrian A.; Wormald, Philip; Lightfoot, Philip |
| Journal of publication | Chemistry of Materials |
| Year of publication | 2008 |
| Journal volume | 20 |
| Journal issue | 21 |
| Pages of publication | 6810 |
| a | 9.3243 ± 0.0018 Å |
| b | 11.391 ± 0.002 Å |
| c | 8.4009 ± 0.0016 Å |
| α | 90° |
| β | 90° |
| γ | 90° |
| Cell volume | 892.3 ± 0.3 Å3 |
| Cell temperature | 150 ± 2 K |
| Ambient diffraction temperature | 150 ± 2 K |
| Number of distinct elements | 5 |
| Space group number | 72 |
| Hermann-Mauguin space group symbol | I b a m |
| Hall space group symbol | -I 2 2c |
| Residual factor for all reflections | 0.0271 |
| Residual factor for significantly intense reflections | 0.0254 |
| Weighted residual factors for significantly intense reflections | 0.0677 |
| Weighted residual factors for all reflections included in the refinement | 0.0702 |
| Goodness-of-fit parameter for all reflections included in the refinement | 0.965 |
| Diffraction radiation wavelength | 0.7749 Å |
| Diffraction radiation type | synchrotron |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 178377 (current) | 2016-03-21 | cif/4/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/00. |
4001270.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4001270.cif |
| 91935 | 2013-12-29 | cod/ (saulius@koala.ibt.lt) Adding DOIs that could be assigned unambiguously to the rest of COD CIFs. |
4001270.cif |
| 41956 | 2012-03-13 | ../uploads/cif-deposit/cod/cif Adding structures of 4001270, 4001271 via cif-deposit CGI script. |
4001270.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.